ECOVYLOPET® EMC2301E
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | ECOVYLOPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVITBV_ECOVYLOPET-EMC2301E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Features 1. Having made significant improvement in appearances, fluidity and mold release easiness, ECOVYLOPET® can be processed much easier than general PET for injection molding. 2. It is adaptable for large auto-parts and industrial product parts. 3. With a specific miscibility method, its impact resistance has greatly been enhanced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00 mm | 1.2 | % | |
| Across Flow : 2.00 mm | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Strength (Yield) | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 205 | °C | ASTM D648 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Flexibility Modulus | 3.7 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PBT T1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Formolene® L63568U | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| LUVOCOM® 1200-8777 | Lehmann & Voss & Co. | ABS | LUVOCOM® |
| PLUSTEK PA303G43 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| TECACOMP® PA66 CF40 black 3623 | Ensinger GmbH | Nylon 66 | TECACOMP® |