PREPERM® L300
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Premix Oy |
| Trademark: | PREPERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OUFQIS_PREPERM-L300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PREPERM® L300 is a special compound with elevated dielectric constants of 3.0. PREPERM® L300 is based on Premix proprietary PPE technology. Extremely low dissipation factor (0.0005) makes PREPERM® L300 an excellent material for high frequency applications. PREPERM® L300 offers stable dielectric constant over wide frequency and wide temperature range. PREPERM® retains its physical properties at very low (-78°C) temperatures. PREPERM® L300 can be injection moulded or extruded. Applications include structural parts for antennas in base stations, point to point, wlan, mobile phones etc. Devices made out of PREPERM® L300 can operate at very high frequencies as PREPERM® L300 offers stable performance even at 120 GHz. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | ISO 527-2 |
| 4.00 mm | 47.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | ISO 527-2 |
| Fracture, 4.00mm | 30 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ISO 180 | ||
| -78°C | 16 | kJ/m² | ISO 180 |
| -20°C | 20 | kJ/m² | ISO 180 |
| 23°C | No Break | ISO 180 | |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -78°C | No Break | ISO 180 | |
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 176 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 155 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 193 | °C | ISO 306/A50 |
| -- | 161 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 3.00 | Internal method | |
| Dissipation Factor (1.00 GHz) | 5.0E-4 | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (4.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 60.0 - 80.0 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 260 - 280 | °C | |
| Die Temperature | 260 - 300 | °C |
| Extrusion instructions |
|---|
| Tool / roll temperature : 60 - 180°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2607 | Covestro - Polycarbonates | PC | Makrolon® |
| Tecomid® NB40 NL IX | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Unipren® Elastomers A3 PRTA010 70A UP321 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Boda BDTL30P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EPOXIDUR® EP 3585 | RASCHIG GmbH | Epoxy | EPOXIDUR® |