Order Products : sales@su-jiao.com
AKROMID® B3 GFM 15/25 black (1312)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OTXuHI_AKROMID-B3-GFM-15-25-black-1312-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability Application areas are optical demanding covers in the automotive, electric and furniture industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 6.5 | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.8 | % | ISO 1110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Index | IEC 216 | ||
| 50% Loss of Tensile Strength, 20000 hr | 130 to 150 | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 160 to 175 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 40 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7000 | MPa | ISO 178 |
| Flexural Stress 2 | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 216 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Melting Temperature 3 | 222 | °C | DIN EN 11357-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravalene CR L 5241 | Ravago Group | LDPE | Ravalene |
| Novamid® 1030J | DSM Engineering Plastics | Nylon 6 | Novamid® |
| Boda BDF-LB2701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Chemlon® MDF863 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| LEXAN™ LUX9616G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |