SUPREME Specialty PS SP8001
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OSt1G6_SUPREME-Specialty-PS-SP8001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUPREME Specialty PS SP8001 is a High Impact Polystyrene product. It can be processed by extrusion or thermoforming and is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of SUPREME Specialty PS SP8001 include containers, appliances, bags/liners and food contact applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 3.20 mm, Injection Molded) | 0.20 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 1100 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 34.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Injection Molded) | 90 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6031N-SI | TSRC Corporation | TPE | T-Blend® |
| Colorite G Series 9011G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| CP PRYME® PC/ABS PCA100 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| EXCELLOY TK15 | Techno Polymer Co, Ltd. | ABS+PBT | EXCELLOY |
| POLYFORT® FPP 1902 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |