Ultramid® A3HG7 BK00564
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OSXCLV_Ultramid-A3HG7-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3HG7 BK00564 is a 35% glass fiber reinforced, pigmented black injection molding PA66 grade. Applications Typical applications include machinery components and housings of high stiffness and dimensional stability such as gears, solenoid valve housings, electrical flow heaters, trailing cable attachments, as well as electrically insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versalloy™ HC 9220-70 | PolyOne Corporation | TPE | Versalloy™ |
| Vitaster® US10NT6182 | Jackdaw Polymers | PBT | Vitaster® |
| AEI TP519C | AEI Compounds Limited | PE, Unspecified | AEI |
| Latiblend 6252 H2 G/30 | LATI S.p.A. | Nylon+PP | Latiblend |
| LTP PA6125 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |