ISPLEN® PM 281 BV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OSSh5s_ISPLEN-PM-281-BV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer, 20% mineral fillers reinforced and good melt flow rate. ISPLEN® PM281 BV was designed showing a high stiffness with a good impact resistance, and a low warpage and high shrinkage behaviour. It shows really good gloss surface and an excellent scratch resistance. The product is UV stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.82 to 0.85 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | |
| Break | 21.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 18 | % | |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.5 | kJ/m² | |
| 0°C | 2.5 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 32 | kJ/m² | |
| 0°C | 40 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 63.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A120 |
| -- | 83.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® PP 1329 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Badamid® T70 GF30 | Bada AG | Nylon 6/6T | Badamid® |
| BLUESTAR® POM BS090A | Beijing Ranger Chemical Co., Ltd. | Acetal (POM) Copolymer | BLUESTAR® POM |
| Celstran® PPS-CF30-01 | Celanese Corporation | PPS | Celstran® |
| Sylvin 916VO Grey 9371 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |