Ultramid® A3HG6 HR BK23591
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ORFksT_Ultramid-A3HG6-HR-BK23591.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3HG6 HR BK23591 is a 30% glass reinforced, pigmented black, injection molding PA66 grade. It offers good resistance to hydrolysis. Applications Typical applications include automotive radiator mounting frame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 225 | 175 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 6800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Break, -40°C | 240 | 231 | MPa | |
| Break, 23°C | 190 | 120 | MPa | |
| Tensile Strain (Break, 23°C) | 3.2 | 5.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8700 | 5800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 275 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 11 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 13 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C | |
| RTI Elec (1.50 mm) | 65.0 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
| RTI Str (1.50 mm) | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 5.60 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.14 | 0.23 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TH 8000D | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| Ultramid® 66 H2 G/25-V0KB1 BK3324 | BASF Corporation | Nylon 66 | Ultramid® |
| HiFill FR® ABS/PBT FR | Techmer Engineered Solutions | ABS+PBT | HiFill FR® |
| OTECH PVC OW834 - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| POCAN® KU 1-7301 000000 | LANXESS Corporation | PBT | POCAN® |