Generic Polyester, TS - Glass\Mineral
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OR5eHc_Generic-Polyester-TS---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester, TS - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.85 - 2.02 | g/cm³ | ASTM D792 |
| 23°C | 1.67 - 1.91 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.070 - 0.35 | % | ASTM D955 |
| 23°C | -0.050 - 0.16 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.099 - 0.19 | % | ASTM D570 |
| Saturated, 23°C | 0.30 - 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 29 - 46 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10700 - 14000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 34.5 - 49.0 | MPa | ASTM D638 |
| Yield, 23°C | 22.1 - 92.6 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.0 - 1.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8630 - 11100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 108 - 127 | MPa | ASTM D790 |
| 23°C | 65.7 - 190 | MPa | ISO 178 |
| Compressive Strength (23°C) | 165 - 180 | MPa | ASTM D695 |
| Poisson's Ratio (23°C) | 0.30 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 - 82 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 140 - 420 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 257 - 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 - 202 | °C | ISO 75-2/A |
| Continuous Use Temperature | 164 - 171 | °C | ASTM D794 |
| Glass Transition Temperature | 161 - 172 | °C | DSC |
| CLTE - Flow | 1.0E-5 - 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 - 2.5E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 7.5E+14 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 13 - 16 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 5.17 - 5.53 | ASTM D150 | |
| Dissipation Factor (23°C) | 7.0E-3 - 0.020 | ASTM D150 | |
| Arc Resistance | 179 - 190 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 - 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 750 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 - 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 142 - 152 | °C | |
| Injection Pressure | 4.65 - 9.38 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyester, TS - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 HF TFE 10 | RTP Company | PC | RTP |
| Evermore PUR B-625NTA | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Ferro PP LPP20BN38WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| EPIMIX POM PTFE 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| INNOMID® CS 6-9000 | Inno-Comp Ltd. | Nylon 6 Alloy | INNOMID® |