| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OR4AX1_Generic-PVC-Rigid.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PVC, Rigid This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 - 1.47 | g/cm³ | ASTM D792 |
| 23°C | 1.32 - 1.62 | g/cm³ | ISO 1183 |
| -- | 0.801 - 0.802 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.52 - 0.65 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 1.4 - 60 | g/10 min | ASTM D1238 |
| Spiral Flow | 54.9 - 119 | cm | |
| Molding Shrinkage - Flow (23°C) | 0.35 - 0.41 | % | ASTM D955 |
| K-Value (23°C) | 64.9 - 65.3 | ISO 1628-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 89 - 117 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 75 - 85 | ASTM D2240 | |
| 23°C | 44 - 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2170 - 3380 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 38.3 - 50.5 | MPa | ASTM D638 |
| Yield, 23°C | 37.9 - 45.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 41.1 - 50.8 | MPa | ASTM D638 |
| Fracture, 23°C | 32.0 - 42.4 | MPa | ISO 527-2 |
| 23°C | 12.5 - 50.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.6 - 190 | % | ASTM D638 |
| Fracture, 23°C | 78 - 150 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2290 - 3210 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 65.3 - 94.1 | MPa | ASTM D790 |
| Yield, 23°C | 61.6 - 87.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.9 - 21 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 16 - 1100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 50 - 170 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 14.7 - 36.2 | J | ASTM D3029 |
| Tensile Impact Strength (23°C) | 12.8 - 191 | kJ/m² | ASTM D1822 |
| Drop Impact Resistance (23°C) | 6.67 - 202 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 64.7 - 81.3 | °C | ASTM D648 |
| 0.45 MPa, annealed | 69.6 - 81.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.6 - 76.5 | °C | ASTM D648 |
| 1.8 MPa, annealed | 61.5 - 78.3 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 74.8 - 99.0 | °C | ASTM D1525 |
| -- | 71.5 - 89.9 | °C | ISO 306 |
| Melting Temperature | 166 - 184 | °C | |
| CLTE - Flow | 5.3E-5 - 7.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.16 | W/m/K | ASTM C177 |
| RTI Elec | 50.0 - 95.4 | °C | UL 746 |
| RTI Imp | 50.0 - 85.0 | °C | UL 746 |
| RTI | 50.0 - 95.4 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 35 - 38 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 73.5 - 87.9 | % | ASTM D1003 |
| Haze | 3.8 - 6.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 162 - 163 | °C | |
| Middle Temperature | 182 | °C | |
| Front Temperature | 187 - 188 | °C | |
| Nozzle Temperature | 185 | °C | |
| Processing (Melt) Temp | 200 - 206 | °C | |
| Mold Temperature | 32.0 - 32.2 | °C | |
| Injection Pressure | 108 - 110 | MPa | |
| Back Pressure | 0.839 - 0.866 | MPa | |
| Screw Speed | 52 - 53 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC, RigidThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 - 166 | °C | |
| Cylinder Zone 2 Temp. | 154 - 166 | °C | |
| Cylinder Zone 3 Temp. | 160 - 177 | °C | |
| Cylinder Zone 4 Temp. | 166 - 182 | °C | |
| Melt Temperature | 182 - 188 | °C | |
| Die Temperature | 175 - 191 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC, RigidThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SG3181S | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| Telcar® TL-1081A | Teknor Apex Company | TPE | Telcar® |
| Cogegum® AFR/920-UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| ISORENE™ AA9C1-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| Karina IVORY PVC -E 810D35/ 1-C-AC-AS-LMP (034128-00) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |