RTP 801
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OQxgiP_RTP-801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 - 1.2 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 - 6.0 | % | ASTM D638 |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 132 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 182 - 218 | °C | |
| Mold Temperature | 79.4 - 107 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-131G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Pearlthane® D11H95S | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| TechnoElast S A6002 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |
| Sylvin 9067-60 Black 295 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® DP 7318 000000 | LANXESS GmbH | PBT | POCAN® |