Lustran® ABS 448
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OQaQCH_Lustran-ABS-448.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS 448 resin is a high-gloss, high-impact injection molding grade of ABS (acrylonitrile butadiene styrene). In addition to a good balance of physical properties, it provides heat stability and very good moldability. Lustran ABS 448 is tougher than Lustran ABS 248 resin. It is used in home appliances for floor care housings, vacuum cleaner housings, and kitchen electrical appliance housings; lawn and garden equipment; and power tool housings. As with any product, use of Lustran ABS 448 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 12 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.1 | MPa | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 64 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7mm | 91.7 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 99.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 81.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm, molded | 101 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 94.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.47 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.47 mm) | 80.0 | °C | UL 746 |
| RTI (1.47 mm) | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| 5.99 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 266 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 7760 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| TRIREX® 3017PJ | Samyang Corporation | PC | TRIREX® |
| Zenite® 5130L | Celanese Corporation | LCP | Zenite® |
| Esterlloy™ AT900 | Asahi Kasei Chemicals Corporation | ABS Alloy | Esterlloy™ |
| Sylvin 7868-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |