YUNCON® N90-01

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	YunNan YunTianHua Co., Ltd.
Trademark:	YUNCON®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OQZod4_YUNCON-N90-01.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Standard-flow grade, with minimized mold deposit

General Information
Features	Acid Resistant Bacteria Resistant Base Resistant Copolymer Fatigue Resistant Good Abrasion Resistance Good Chemical Resistance Good Dimensional Stability Good Electrical Properties Good Flow High Hardness High Stiffness Low Friction Low Warpage Solvent Resistant
Uses	Automotive Electronics Automotive Exterior Parts Automotive Under the Hood Bearings Fittings Gears Pump Parts Thin-walled Parts Valves/Valve Parts Wheels
Agency Ratings	DMF Unspecified Rating EN 71-3 FDA Unspecified Rating NSF Unspecified Rating UL Unspecified Rating
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	9.0	g/10 min	ISO 1133
Water Absorption (23°C, 24 hr)	0.30	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2650	MPa	ISO 527-2
Tensile Stress (Yield)	61.0	MPa	ISO 527-2
Tensile Strain (Break)	35	%	ISO 527-2
Flexural Modulus	2550	MPa	ISO 178
Flexural Stress	89.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	5.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	95.0	°C	ISO 75-2/A

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0 to 90.0	°C
Drying Time	3.0 to 4.0	hr
Rear Temperature	160 to 180	°C
Middle Temperature	170 to 200	°C
Front Temperature	190 to 210	°C
Nozzle Temperature	180 to 210	°C
Processing (Melt) Temp	180 to 210	°C
Mold Temperature	60.0 to 90.0	°C
Injection Pressure	50.0 to 100	MPa
Holding Pressure	30.0 to 80.0	MPa
Back Pressure	0.00 to 0.500	MPa
Screw Speed	50 to 120	rpm

Extrusion	Nominal Value	Unit
Melt Temperature	180 to 190	°C

Resin Grade	Manufacturer	Category	Trademark
NYLOY® MG-8030N-V 60N1	Nytex Composites Co., Ltd.	Nylon 66	NYLOY®
ASTALAC™ ABS GSM	Marplex Australia Pty. Ltd.	ABS	ASTALAC™
Axiall PVC 18731	Axiall Corporation	PVC, Flexible	Axiall PVC
EnviroPro 9003	West Michigan Compounding	PP Copolymer	EnviroPro
LNP™ LUBRICOMP™ ZL003 compound	SABIC Innovative Plastics	PPE+PS	LNP™ LUBRICOMP™