WPP PP PRC25TF2HF-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OQEtoX_WPP-PP-PRC25TF2HF-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PRC25TF2HF-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 30.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/5 |
| Yield | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 2300 | MPa | ASTM D790 |
| -- 3 | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 33 | J/m | ASTM D256 |
| 23°C | 4.0 | kJ/m² | ISO 180/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 69.0 | °C | ISO 75-2/Af |
| 1.8 MPa, annealed | 94.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3035 JU5 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Keyflex® BT 1035D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| LINATHENE® LL115C | USI Corporation | LLDPE | LINATHENE® |
| Lumid® HI5006A(W) | LG Chem Ltd. | Nylon 6+ABS | Lumid® |
| Lupoy® SC1004L | LG Chem Ltd. | PC | Lupoy® |