ULTEM™ 2210 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OPyY9F_ULTEM-2210-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 8.4 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6890 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 140 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 6890 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 100 mm Span) | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 211 | °C | |
| Vicat Softening Temperature | 226 | °C | ASTM D1525 6 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI Str | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.406 mm | V-0 | ||
| 1.91 mm | 5VA | ||
| Oxygen Index | 50 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 1.30 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AG15A0 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| SLOVAMID® 6 HI/1 TLS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Ultradur® B 4300 G6 High Speed | BASF Corporation | PBT | Ultradur® |
| Karina CLEAR PVC COMPOUND 35/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kazan LDPE 102-05K | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |