Geon™ Vinyl Rigid Extrusion L7005
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OP03Hm_Geon-Vinyl-Rigid-Extrusion-L7005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon L7005 is recommended for whites and light pastel colors only. Not recommended for horizontal applications such as railing and decking except in white. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-42434-33 | ASTM D4216 | |
| PVC Cell Classification | 15354 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2850 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 43.2 | MPa | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 84.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 590 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 73.4 | J/cm | ASTM D4226 |
| 23°C 4 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 73.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 6 | 71.1 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 7 | 74.4 | °C | ASTM D648 |
| CLTE - Flow | 6.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.749 mm, ALL) | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 注释：物理属性基于L7005 tan 3210 样品。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 50 deg.C |
| 6 . | Annealed at 50 deg.C |
| 7 . | Annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Polyamide Elastomer XPA 9063F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| Amilan® CM3004-V0 | Toray Resin Company | Nylon 66 | Amilan® |
| GAPEX® APP40GP03BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| LNP™ LUBRICOMP™ AG5LT2 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| MARPOL® mLLF 801-B | Marco Polo International, Inc. | mLLDPE | MARPOL® |