DESLON™ 6 DSC102GK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOgYNG_DESLON-6-DSC102GK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC102GK is one of the brands which made by Polyamide6 that filled Glass Fiber 35% and enhanced impact goods. It provides good mechanical property, excellent strength property and elasticity property. Applications: DESLON™ DSC102GK is one of the most-used for mechanical properties of high strength, elasticity and impact resistance good, such as Drive Main Chain, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 147 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 8140 | MPa | ASTM D790 |
| Flexural Strength | 216 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Arc Resistance | 170 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 30 to 60%Pressure 1st: 30 to 70%Pressure 2nd: 30 to 70Holding Pressure: 10 to 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP LGF 40 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Sanren T300 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Blendfor® A 4000 GF/20 NATURALE | SO.F.TER. SPA | PC+ABS | Blendfor® |
| Borealis PP SA233CF | Borealis AG | PP Random Copolymer | Borealis PP |
| PENTESTER BT H black | PENTAC Polymer GmbH | PBT | PENTESTER BT |