NYCOA Polyamide 2366
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOVlKe_NYCOA-Polyamide-2366.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2366 is an extremely flexible and transparent Nylon copolymer specifically developed for extrusion applications such as high-end fishing line, and flexible tubing. NYCOA 2366 possesses an extremely high degree of softness, flexibility, and transparency compared to standard monofilament grade nylons. NYCOA 2366 can be easily extruded on most equipment. This product is available in heat and light stable grades. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D638 |
| Flexural Modulus 3 | 250 | MPa | ASTM D790 |
| Flexural Strength 4 | 13.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 860 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 203 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ LLDPE LL800 | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |
| TECHLEN M1400 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Nypol® PA A3 G20 NTLA010 NR401 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ALTECH® PA66 A 1000/109 YL2492-12LS | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| ExxonMobil™ PP7033E3 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |