Telcar® TL-2522C
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOQh95_Telcar-TL-2522C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-2522C is a general purpose thermoplastic elastomer designed for the industrial market. Telcar TL-2522C is a low hardness, low density grade suitable for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 45 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 43 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 2.80 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 3.67 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 3.76 | MPa | ASTM D412 |
| Tensile Strength 4 | ASTM D412 | ||
| Transverse flow : Fracture | 4.63 | MPa | ASTM D412 |
| Flow : Fracture | 4.16 | MPa | ASTM D412 |
| Tensile Elongation 5 | ASTM D412 | ||
| Transverse flow : Fracture | 440 | % | ASTM D412 |
| Flow : Fracture | 220 | % | ASTM D412 |
| Tear Strength 6 | ASTM D624 | ||
| Transverse flow | 35.0 | kN/m | ASTM D624 |
| Flow | 24.7 | kN/m | ASTM D624 |
| Compression Set 7 | ASTM D395B | ||
| 23°C, 22 hr | 24 | % | ASTM D395B |
| 70°C, 22 hr | 43 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Mouth die C, 510mm/min |
| 6 . | C mold, 510mm/min |
| 7 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 GR30 NL MB | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Nymax™ 1010 A Black 13 | PolyOne Corporation | Nylon 6 | Nymax™ |
| Celanex® 1602Z | Celanese Corporation | PBT | Celanex® |
| Cyclics® Formlite™ | Cyclics Corporation | TP, Unspecified | Cyclics® |
| Lupox® GP1000H | LG Chem Ltd. | PBT | Lupox® |