EQUATE PE EPDA-5040
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | EQUATE Petrochemical Company KSCC |
| Trademark: | EQUATE PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOGy1a_EQUATE-PE-EPDA-5040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EPDA-5040 is a high molecular weight high density polyethylene copolymer resin designed for non-pressure gravity pipe applications. It has a good balance of flexibility, ductility, stiffness and toughness for exceptional freedom in pipe designing. It also offers excellent resistance to environmental stress cracking. EPDA-5040 has been adequately stabilized for long-term service life durability. The product's broad molecular weight distribution provides for easy procesability in to pipe with smooth pipe surfaces and good dispersion of pigments, and carbon black for protection against UV light. EPDA-5040 applications include gravity pipe systems for underground drainage and sewage. It is suitable for both straight and structured wall pipes. In addition it can also be used for extruding electrical conduits. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | > 1000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Elongation (Break) | > 750 | % | ASTM D638 |
| Flexural Modulus | 1180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | 17.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 99.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature | 135 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 113 | °C | Internal Method |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 205 | °C | |
| Cylinder Zone 3 Temp. | 205 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Adapter Temperature | 205 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 205 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nymax™ GF1200 A43 NATURAL | PolyOne Corporation | Nylon 66 | Nymax™ |
| APEX® 410 | Teknor Apex Company | PVC, Flexible | APEX® |
| Durethan® BG 30 X F30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Gallonprene® GP520-6007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HOPELEN SFI-151 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |