VITAMIDE® AS30VN6457
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OO9WTl_VITAMIDE-AS30VN6457.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AS30VN6457 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 1.5 | % | Internal Method |
| Water Absorption | |||
| 24 hr | 1.5 | % | ASTM D570 |
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Break | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 4.50 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | > 230 | °C | ISO 306/B50 |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- 3 | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 700 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-1950-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Ultramid® B40 | BASF Corporation | Nylon 6 | Ultramid® |
| NYLAFORCE® B 60 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | NYLAFORCE® |
| LNP™ THERMOTUF™ RF002I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |
| Sylvin 8200-90 Clear 8395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |