TIPELIN® FB 472-02
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OMgeFi_TIPELIN-FB-472-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN FB 472-02 is a high density polyethylene copolymer (with hexen-1 as comonomer) grade. The film made of this type has good mechanical properties. The grade contains antioxidants and acid scavenger. Applications TIPELIN FB 472-02 is recommended for films, bags, shopping bags, garbage bags and blend component for LDPE in shrink films. TIPELIN FB 472-02 is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.68 | g/10 min | |
| 190°C/21.6 kg | 40 | g/10 min | |
| 190°C/5.0 kg | 2.7 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Compression Molded) | 1250 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 22.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 24.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 67.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 800 | % | |
| TD : Break, 40 µm, Blown Film | 900 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 55 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, Blown Film | 0.24 | N | |
| TD : 40 µm, Blown Film | 2.9 | N | |
| Spencer Impact - Blown Film (40.0 µm) | 28.0 | MPa | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time - Compression Molded (200°C) | 50 | min | EN 728 |
| Vicat Softening Temperature | 124 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TEA A 6003 ACN1 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TEA |
| Bayfill® 369 (46.9:100) | Covestro - PUR | PUR-MDI | Bayfill® |
| APEX® 87-L417D-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Keysor PVC KC1110 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| 3M™ Dyneon™ PTFE Compound TF 7681 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |