Geon™ HTX M6829
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OLIg2q_Geon-HTX-M6829.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ HTX M6829 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ HTX M6829 include electrical/electronic applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Spiral Flow | 86.4 | cm | |
| Molding Shrinkage - Flow | 0.40 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2340 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 39.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 370 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 82.8 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 88.9 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 77.2 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 86.1 | °C | |
| Vicat Softening Point | 91 | °C | |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm, ALL) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 204 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 35.2.0 | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| Celanex® 4300LM | Celanese Corporation | PBT | Celanex® |
| ASTALAC™ ASA 304 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| Flexane® Fast Cure Rubber Repair Putty | Devcon | PUR, Unspecified | Flexane® |
| Monprene® CP-17260 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |