SABIC® LLDPE 6135BE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OKDOft_SABICLLDPE6135BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6135BE is a medium density grade typically used in high demanding extrusion segments like e.g. sheet and more specific geo-membranes. The grade is a hexene-1 copolymer combining good extrusion performance, mechanical properties and ESCR with low migration figures because of the increased density compared to LLDPE grades. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.80 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 2.4 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 54 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.60mm, molded) | 620 | MPa | ISO 527-2/200 |
| Tensile Stress (yield, 1.60mm, molding) | 18.0 | MPa | ISO 527-2/200 |
| Tensile Strain | ISO 527-2/200 | ||
| Yield, 1.60mm, molded | 12 | % | ISO 527-2/200 |
| Fracture, 1.60mm, molded | > 700 | % | ISO 527-2/200 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, molded | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C, molded | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 118 - 122 | °C | DIN 53765 |
| Oxidation Induction Time - Compression Molded (210°C, 1.60 mm) | > 50 | min | EN 728 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Constant Tensile Load - Compression Molded (1.60 mm) | > 2.7 | month | ASTM D5397 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4605 TFE 10 | RTP Company | SPS | RTP |
| Shin-Etsu RTV KE-3479 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Nypol® PA A3 G20 NTLA010 NR401 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DENITER 1010 | Vamp Tech | PBT | DENITER |
| OMIKRON XLT 50 NAT | TECNOPOL | PP Copolymer | OMIKRON |