Order Products : sales@su-jiao.com
Arlon® 55LM
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OHgbC3_Arlon-55LM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55LM is an epoxy laminate and prepreg system, reinforced with non-woven aramid fiber, with substantially lower moisture absorption compared with conventional epoxy/aramid products, even in high-humidity environments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792A |
| Water Absorption (24 hr) | 0.20 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 337 | °C | |
| Initial | 328 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength 1 | 1.1 | kN/m | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 2 | 4.5 | % | Internal Method |
| T260 | > 1.0 | hr | Internal Method |
| T288 | > 1.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 276 | MPa | Internal Method |
| Flexural Strength | 14.5 | MPa | Internal Method |
| Compressive Modulus | 207 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 160 | °C | Internal Method |
| CLTE - Flow | |||
| -- 3 | 1.0E-5 to 1.2E-5 | cm/cm/°C | Internal Method |
| < 160°C 4 | 9.8E-5 | cm/cm/°C | Internal Method |
| > 160°C 5 | 2.5E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.20 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | 1.0E+15 | ohms | Internal Method |
| Volume Resistivity 7 | 1.0E+16 | ohms·cm | Internal Method |
| Dielectric Strength | > 49 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 3.80 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.022 | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Thermal Stress |
| 2 . | Z-axis |
| 3 . | Y-axis |
| 4 . | Z-axis |
| 5 . | Z-axis |
| 6 . | E24/125 |
| 7 . | E24/125 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE BF-0323/12HC | Braskem | LDPE | Braskem PE |
| Axiall PVC 19912 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DOMAMID® A1-006-N2-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| PENTAMID AB MA30T H grau 7035/1 | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| OTECH TPO OTR2087-Molding | OTECH Corporation | TPE | OTECH TPO |