NYCOA Polyamide 2001
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OHEtZC_NYCOA-Polyamide-2001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2001 is a flexible, high viscosity, impact modified Nylon 6 resin for extrusion processing and injection molding. NYCOA 2001 is a high viscosity resin that features a very high resistance to impact, high melt strength, and exceptional toughness. NYCOA 2001 is recommended for extruded profiles and tubes requiring very good toughness, even at low temperatures. Injection molding applications include safety guards, and soft-touch appliance parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 235°C/1.0 kg | 0.52 | g/10 min | ASTM D1238 |
| 235°C/5.0 kg | 6.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 67.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 1690 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 55.6 | °C | ASTM D648 |
| Melting Temperature | 218 | °C |
| Additional Information |
|---|
| The value listed as Melting Point was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638: 300+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 235 - 252 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218 V40 BLACK 21 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| NILAMID® C3 HH GF60 | Nilit Plastics | Nylon 66/6 | NILAMID® |
| Elvacite® 2013 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| PLUSTEK PB142 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 4200-88 Clear Green 3207 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |