NEONIT® SK60 L8F
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | SBHPP |
| Trademark: | NEONIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OGzU0B_NEONITSK60L8F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NEONIT® SK60 L8F is a medium flow long glass fiber reinforced epoxy molding compound with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.86 | g/cm³ | ISO 1183 |
| Apparent Density | 0.50 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.090 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Post Shrinkage | -0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21000 | MPa | ISO 527-2 |
| Tensile Stress | 119 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 17000 | MPa | ISO 178 |
| Flexural Stress | 223 | MPa | ISO 178 |
| Compressive Stress | 227 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 52 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 165 | °C | TMA |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 8.0E-6 | cm/cm/°C | TMA |
| Lateral | 5.9E-5 | cm/cm/°C | TMA |
| Thermal Conductivity | 0.56 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 38 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C, 1 MHz) | 0.022 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 55A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| Ablebond 84-1LMISR4 | Henkel Ablestik | Epoxy | Ablebond |
| Karina CLEAR PVC COMPOUND 80/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND FADA 45-YAT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ 9X02785 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |