Ebalta LH 22 / GR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OFvgfg_Ebalta-LH-22-GR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 to 90 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 4150 to 4450 | MPa | ISO 178 |
| Flexural Stress | 95.0 to 115 | MPa | ISO 178 |
| Compressive Stress | 101 to 103 | MPa | ISO 604 |
| Flexural Strain at Flexural Strength | 3.0 to 3.8 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 13 to 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 63.0 to 67.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 23 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.32 to 1.38 | g/cm³ | |
| Viscosity (25°C) | 1.1 to 1.5 | Pa·s | |
| Curing Time (20°C) | 12 to 16 | hr | |
| Pot Life 1(20°C) | 25 to 30 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QAMAR CD18N | SPDC Ltd. | LLDPE | QAMAR |
| Daicel PP PT6N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Daelim Po1y® PA-124VS | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Sumiliteresin® PR-51618G | SBHPP | Phenolic | Sumiliteresin® |
| StarPet® 8030-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPet® |