Order Products : sales@su-jiao.com
Leona™ 90G55
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OFnnZV_Leona-90G55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 90G55 is a Polyamide 66 (Nylon 66) product filled with 55% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 90G55 include automotive, construction applications and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.64 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.1 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.1 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 95 | 88 | ||
| R-Scale | 120 | 115 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 18600 | 14800 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 232 | 163 | MPa | ISO 527-2 |
| -- | 221 | 181 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.0 | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 15700 | 12700 | MPa | ASTM D790 |
| 23°C | 15400 | 12300 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 348 | 284 | MPa | ASTM D790 |
| 23°C | 394 | 269 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 13 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 82 | 71 | kJ/m² | ISO 179 |
| Notched Izod Impact | 110 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Specific Heat | 1930 | -- | J/kg/°C | |
| Thermal Conductivity | 0.30 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 450 | -- | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MKF 3010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SITRADUR 35E / C01000 | SITRAPLAS GmbH | PBT | SITRADUR |
| Starflam AFR460B | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Borealis PE FG5190 | Borealis AG | LLDPE | Borealis PE |
| POLYFLON™ M-112 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |