BFI 3271
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Blueridge Films Inc. |
| Trademark: | BFI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OEiHFq_BFI-3271.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BFI 3271 is a Polypropylene Impact Copolymer (PP Impact Copolymer) material. It is available in North America for blow molding. Primary attribute of BFI 3271: Copolymer. Typical application of BFI 3271: Film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| MD : Blown Film | 2410 | MPa | |
| TD : Blown Film | 4140 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, Blown Film | 152 | MPa | |
| TD : Break, Blown Film | 241 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, Blown Film | 150 | % | |
| TD : Break, Blown Film | 60 | % | |
| Water Vapor Transmission Rate (38°C, Blown Film, 90% RH) | 0.12 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 160 to 165 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 1.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP PP CO 008 NB | Amco Polymers | PP Impact Copolymer | PRIMATOP |
| SABIC® LLDPE MG500026 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Baoding 76T85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| CALIBRE™ 2061-6 | Trinseo | PC | CALIBRE™ |
| LUVOCOM® 1105-7373 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |