Order Products : sales@su-jiao.com
Alathon® M4612
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OEGH2Y_Alathon-M4612.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M 4612 is a copolymer that provides outstanding stress crack resistance and low temperature impact strength. Typical applications include food containers, seat hinges, tube headers and parts requiring high ESCR. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Spiral Flow | 19.6 | cm | Internal Method |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 10% Igepal | 33.6 | hr | |
| 100% Igepal | 552 | hr |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 807 | MPa | |
| 1% Secant | 636 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 23.1 | MPa | |
| Break | 23.9 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 12 | % | |
| Break | 550 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1010 | MPa | |
| 1% Secant | 931 | MPa | |
| 2% Secant | 772 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Peak Melting Temperature | 128 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8200 HS | BASF Corporation | Nylon 6 | Ultramid® |
| Network Polymers Nylon 6604 HS | Network Polymers, Inc. | Nylon 66 | Network Polymers Nylon |
| Abstron KU600 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Hanwha Total PP TB53L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| HiFill® POM CO 0167 S2 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |