AZDEL™ PM10300
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ODtoI6_AZDEL-PM10300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL PM10300 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a generally homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4790 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 5070 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Compressive Strength | 96.5 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 9.49 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 20.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 154 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 11 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.85 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 30 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 550 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 616 J/mPoissons Ratio, ISO 527: 0.238Sheet Thickness, Internal Test Method: 150 milsSpecific Gravity, ASTM D792, Laminated: 1.09Specific Gravity, ASTM D792, Molded: 1.12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA CN-L01 PLA Nucleating Agent | Polyvel Inc. | PLA | Polyvel PLA |
| SLOVAMID® 66 GF 30 FRA 5 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Gallonprene® GP100-3001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| FOZEAS® J9604E | Mitsubishi Chemical Performance Polymers, Inc. | PLA | FOZEAS® |
| K-vinyl 105 Deg C Rating Insulation (Auto) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |