Polytron® A30B041
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ODqTE9_Polytron-A30B041.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% LONG FIBER GLASS REINFORCED,PTFE LUBRICATED, UV STABILIZED BLACK NYLON 6.6 FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| Saturation | 3.4 | % | ASTM D570 |
| Saturation, 23°C | 3.4 | % | ISO 62 |
| Equilibrium | 1.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 170 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9250 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 250 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DuraGrip® DGR 6080NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| Karina CLEAR PVC COMPOUND -E 85/208-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OPNYL OP66UT105 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| OTECH TPO OTE6519 - Cord Jacket | OTECH Corporation | TPO | OTECH TPO |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |