Lupox® GP1000A
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ODgoxk_Lupox-GP1000A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupox®GP1000A is a polybutene terephthalate (PBT) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupox®The main characteristics of the GP1000A are: flame retardant/rated flame. Lupox®The typical application fields of GP1000A are: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2630 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 36 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 170 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 61.0 | °C | ASTM D648 |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 23 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.30 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 245 - 255 | °C | |
| Middle Temperature | 245 - 260 | °C | |
| Front Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 225 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Extrusion instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP 5120C | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Clariant Nylon 6/6 PA-121 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| GAPEX® RPP35EC15BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| HAIPLEN EP70 Y0 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| HiFill FR® PA6/6 GF25 FR-N IM3 | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |