Geon™ Fiberloc™ 81520
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Fiberloc™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ODWGhT_Geon-Fiberloc-81520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ Fiberloc™ 81520 is a Rigid Polyvinyl Chloride product filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Plumbing/Piping/Potable Water. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Spiral Flow | 81.3 | cm | |
| Molding Shrinkage - Flow | 0.050 to 0.15 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7580 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Poisson's Ratio | 0.41 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 110 | J/m | ASTM D256A |
| Unnotched Izod Impact 4(23°C, 3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 77.8 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 700.5 | RTP Company | HDPE | RTP |
| FHR Polypropylene P4C5B-181B | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Huafon JF-P-5250 / JF-I-5222 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| TECACOMP® LCP LDS black 4107 | Ensinger GmbH | LCP | TECACOMP® |
| POLYLAC® PA-777C | CHI MEI CORPORATION | ABS | POLYLAC® |