Honeywell PCTFE P3000HS

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OCv2WI_Honeywell-PCTFE-P3000HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Honeywell PCTFE P-Series HS film is a copolymer poly-chlor-tri-fluoroethylene film. Honeywell PCTFE HS film has the ability to heat seal to itself utilizing impulse sealing methods.

General Information
Features	Copolymer Heat sealable
Uses	Films
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.08	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1030	MPa	ASTM D882
TD	1030	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	62.1	MPa	ASTM D882
TD : Fracture	41.4	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	190	%	ASTM D882
TD : Fracture	230	%	ASTM D882
Water Vapor Transmission	0.17	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	190	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 1.0	%	ASTM D1003

Additional Information
Yield: 4432 in²/lbTensile Strength @ Break, ASTM D 882, MD: 8000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 5000 to 7000 psiElongation @ Break, ASTM 882, MD: 150 to 225%Elongation @ Break, ASTM 882, TD: 200 to 250%Secant Modulus, ASTM D 882, MD: 125000 to 175000 psiSecant Modulus, ASTM D 882, TD: 125000 to 175000 psiGraves Tear (initial), ASTM D 1004, MD: 300 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -3 to -8% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +3 to +8% shrinkageFlammability: Non-flammable

Additional Information

Yield: 4432 in²/lbTensile Strength @ Break, ASTM D 882, MD: 8000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 5000 to 7000 psiElongation @ Break, ASTM 882, MD: 150 to 225%Elongation @ Break, ASTM 882, TD: 200 to 250%Secant Modulus, ASTM D 882, MD: 125000 to 175000 psiSecant Modulus, ASTM D 882, TD: 125000 to 175000 psiGraves Tear (initial), ASTM D 1004, MD: 300 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -3 to -8% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +3 to +8% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
SUMIPEX® EX	Sumitomo Chemical Co., Ltd.	Acrylic (PMMA)	SUMIPEX®
BLUESTAR® PBT 201-G30202	Nantong Zhonglan Engineering Plastics Co., Ltd.	PBT	BLUESTAR®
Avantra® 8530B	PMC Group Polymer Products	PS (HIPS)	Avantra®
EL-Lene™ M3804RW	SCG Chemicals Co., Ltd.	LLDPE	EL-Lene™
Sylvin 9933-75 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin