Hyundai EP PA66 LD130
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OButVe_Hyundai-EP-PA66-LD130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP PA66 LD130 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Asia Pacific. Typical application: Electrical/Electronic Applications. Primary characteristic: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Ash Content | 15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 113 | MPa | ASTM D638 |
| Flexural Modulus | 4410 | MPa | ASTM D790 |
| Flexural Strength | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 243 | °C | ASTM D648 |
| Melting Temperature | 265 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 3.5 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLLAMID A 2700 - A 2730 FV 35 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| Xuchuan A-9072/B-6022 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| GS Pla® AZ91T | Mitsubishi Chemical Performance Polymers, Inc. | Biodeg Polymers | GS Pla® |
| LEXAN™ HPF1 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LOXIM 230 01 V0 | LOXIM Industries Private Limited | PBT | LOXIM |