POCAN® T 7391 000000

Category:	PBT+PET , Polybutylene Terephthalate + PET
Manufacturer:	LANXESS GmbH
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OBT46L_POCANT7391000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT+PET, 45 % glass fibers, injection molding, improved surface finish, increased temperature peak load

General Information
Filler / Reinforcement	Glass fiber reinforced material, 45% filler by weight
Features	Excellent appearance
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.69	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	30.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction : 270°C, 2.00mm ¹	0.80	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.10	%	ISO 294-4
Flow direction : 270°C, 2.00mm ³	0.20	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.10	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C	0.30	%	ISO 62
Equilibrium, 23°C, 50% RH	0.10	%	ISO 62
Viscosity Number (Reduced Viscosity)	80.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	250	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	16000	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	160	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	1.9	%	ISO 527-2/5
Tensile Creep Modulus			ISO 899-1
1 hr	16500	MPa	ISO 899-1
1000 hr	15000	MPa	ISO 899-1
Flexural Modulus ⁵(23°C)	15500	MPa	ISO 178/A
Flexural Stress ⁶(23°C)	260	MPa	ISO 178
Flexural Strain at Flexural Strength (23°C) ⁷	2.1	%

Thermal	Nominal Value	Unit	Test Method
Halving Interval			IEC 60216
-- ⁸	13.5	°C	IEC 60216
-- ⁹	10.2	°C	IEC 60216
-- ¹⁰	10.2	°C	IEC 60216
Temperature index ¹¹			IEC 60216
Electric Strength	155		IEC 60216
Tensile Impact Strength	150		IEC 60216
Tensile Strength	155		IEC 60216

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A 1		IEC 60426
ISO Shortname	PBT+PET, GHMR, 09-160, GF45		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	65	kJ/m²	ISO 179/1eU
23°C	60	kJ/m²	ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	60	kJ/m²	ISO 180/1U
23°C	55	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	225	°C	ISO 75-2/B
1.8 MPa, not annealed	205	°C	ISO 75-2/A
Vicat Softening Temperature	210	°C	ISO 306/B120
Ball Pressure Test (220°C)	Pass		IEC 60695-10-2
Melting Temperature ¹²	225 - 250	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	2.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	8.0E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	0.27	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	28	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	4.30		IEC 60250
23°C, 1 MHz	4.20		IEC 60250
Dissipation Factor			IEC 60250
23°C, 100 Hz	2.0E-3		IEC 60250
23°C, 1 MHz	0.014		IEC 60250
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	HB		UL 94
1.60 mm	HB		UL 94
Glow Wire Flammability Index (2.00 mm)	750	°C	IEC 60695-2-12
Oxygen Index ¹³	21	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	260 - 280	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2; MT 90°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; MT 90°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	Tensile Impact Strength
9 .	Electric Strength
10 .	Tensile Strength
11 .	20000 h
12 .	10°C/min
13 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
TECHNO MUH E1300	Techno Polymer Co, Ltd.	ABS	TECHNO MUH
NEFTEKHIM PE 4133Q (33403)	Nizhnekamskneftekhim Inc.	MDPE	NEFTEKHIM PE
DINALON® B1S25 H	Grupo Repol	Nylon 6	DINALON®
MACOMASS PVC MM-PVC I 1570	MACOMASS Verkaufs AG	PVC, Flexible	MACOMASS PVC
PALMID® R 6 S	pal plast GmbH	Nylon 6	PALMID®