DuraStar™ MN611
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | DuraStar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OAtAi3_DuraStar-MN611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Durastar™ Polymer MN611 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. It contains a mold release to improve ejection. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN611 has very good toughness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 47.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 51.0 | MPa | ASTM D638 |
| Break, 23°C | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 300 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2000 | MPa | ASTM D790 |
| 23°C | 1850 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 65.0 | MPa | ISO 178 |
| Yield, 23°C | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -40°C | 4.8 | kJ/m² | ISO 180 |
| 23°C | 7.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 48.0 | J | |
| 23°C, Energy at Peak Load | 42.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 74.0 | °C | |
| 1.8 MPa, Unannealed | 65.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | ASTM D1003 | ||
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 232 to 277 | °C | |
| Mold Temperature | 16.0 to 38.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 152 UV | RTP Company | PP, Unspecified | RTP |
| Nipoflex® 634 | TOSOH Corporation | EVA | Nipoflex® |
| Axiall PVC 4890 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LNP™ THERMOCOMP™ MF00AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Bergadur™ PB40 G15 Natural TM-Y | PolyOne Corporation | PBT | Bergadur™ |