INEOS PP H20H-00
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OAlLHu_INEOS-PP-H20H-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| H20H-00 is a homopolymer polypropylene designed to provide easy moldability for applications requiring resistance to long-term heat aging. This product is not recommended for taste or odor sensitive applications. Typical applications include appliances, automotive and compounding. This material has been recognized by UL for sustained use at 130°C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 33.0 | MPa | |
| Break | 15.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 12 | % | |
| Break | 170 | % | |
| Flexural Modulus - 1% Secant 3 | 1360 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 36 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 3.54 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 93 | ASTM D2457 | |
| Haze 4(1270 µm) | 72 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Q30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| NEXT REPROCESSED POMC M270-100R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| 4MID® 9A24400 | 4Plas | Nylon 66 | 4MID® |
| ASI POLYPROPYLENE 1692 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| PLUSTEK PB312J6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |