Asrene® UF 1810S1
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Asrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OAA4fg_Asrene-UF-1810S1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Asrene®UF 1810S1 is a linear low density polyethylene product,. It is available in North America, Europe or Asia Pacific. Asrene®UF 1810S1 applications include bags/linings, movies and agriculture. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Cast Film) | 0.060 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 50.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 850 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 30.0 µm | 24.5 | kN/m | ASTM D1922 |
| TD : 30.0 µm | 196.1 | kN/m | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 26.0 | g/100 cm² | ASTM D3354 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 46 | ASTM D2457 | |
| Clarity (30.0 µm, Blown Film) | 28.0 | ASTM D1746 | |
| Haze (30.0 µm, Blown Film) | 20 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 1.5 to 3.5 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 7550 Nat | Nycoa (Nylon Corporation of America) | Nylon 12 | NYCOA Polyamide |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Di-Pak™ R-4525/40 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| ELASTOSIL® LR 3003/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LNP™ LUBRILOY™ D2000AXH compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |