SCHULAMID® 66 GF 25 FR 5 A Datasheet,Nylon 66,A. Schulman Europe-SHANGHAI SUSHENG

Message
25% glass fibre reinforced flame-retardant Polyamide 66 grade; without PBDE and antimony trioxide

General Information
Filler / Reinforcement	Glass Fiber, 25% Filler by Weight
Features	Antimony Free Flame Retardant Good Electrical Properties Good Strength
UL File Number	E86615
Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.59	--	g/cm³	ISO 1183/A

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	10300	8000	MPa	ISO 527-2/1A/1
Tensile Stress (Break)	146	112	MPa	ISO 527-2/1A/5
Tensile Strain (Break)	2.2	3.0	%	ISO 527-2/1A/5
Flexural Modulus ¹	8600	--	MPa	ISO 178
Flexural Stress ²(2.9% Strain)	195	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	10	--	kJ/m²
23°C	10	12	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	52	--	kJ/m²
23°C	52	55	kJ/m²
Notched Izod Impact Strength (23°C)	8.5	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength (23°C)	46	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	> 250	--	°C	ISO 75-2/Bf
1.8 MPa, Unannealed	240	--	°C	ISO 75-2/Af
Ball Pressure Test (200°C)	Pass	--		IEC 60695-10-2
RTI Elec				UL 746
0.500 mm	130	--	°C
0.750 mm	130	--	°C
1.50 mm	130	--	°C
3.00 mm	130	--	°C
RTI Imp				UL 746
0.500 mm	105	--	°C
0.750 mm	105	--	°C
1.50 mm	110	--	°C
3.00 mm	110	--	°C
RTI Str				UL 746
0.500 mm	105	--	°C
0.750 mm	105	--	°C
1.50 mm	120	--	°C
3.00 mm	120	--	°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	4.7E+14	1.4E+13	ohms	IEC 60093
Volume Resistivity	2.7E+14	1.8E+13	ohms·cm	IEC 60093
Comparative Tracking Index	400	--	V	IEC 60112
High Amp Arc Ignition (HAI)				UL 746
0.500 mm	PLC 0	--
0.750 mm	PLC 0	--
1.50 mm	PLC 0	--
3.00 mm	PLC 0	--
Hot-wire Ignition (HWI)				UL 746
0.500 mm	PLC 0	--
0.750 mm	PLC 0	--
1.50 mm	PLC 0	--
3.00 mm	PLC 0	--

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate				ISO 3795
0.500 mm, Self-Extinguishing	0.0	--	mm/min
0.750 mm, Self-Extinguishing	0.0	--	mm/min
1.50 mm, Self-Extinguishing	0.0	--	mm/min
3.00 mm, Self-Extinguishing	0.0	--	mm/min
Flame Rating				UL 94, IEC 60695-11-10, -20
0.500 mm	V-0	--
0.750 mm	V-0	--
1.50 mm	V-0 5VA	--
3.00 mm	V-0 5VA	--
Glow Wire Flammability Index				IEC 60695-2-12
0.500 mm	960	--	°C
0.750 mm	960	--	°C
1.50 mm	960	--	°C
3.00 mm	960	--	°C
Glow Wire Ignition Temperature				IEC 60695-2-13
0.500 mm	900	--	°C
0.750 mm	900	--	°C
1.50 mm	900	--	°C
3.00 mm	930	--	°C
Oxygen Index	34	--	%	ISO 4589-2

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Category:	Nylon 66 , Polyamide 66
Manufacturer:	A. Schulman Europe
Trademark:	SCHULAMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	O9AcWy_SCHULAMID-66-GF-25-FR-5-A.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 605 FR	RTP Company	ABS	RTP
Stirol UPM-0703 E (1s.)	JSC CONCERN STIROL	PS (HIPS)	Stirol
TES J-50/20/RG	Techmer Engineered Solutions	PC	TES
OP - PEI 40GF	Oxford Polymers	PEI	OP - PEI
KMI PP KM-4494ZW	KMI Group, Inc.	PP Impact Copolymer	KMI PP