EcoBlend® HCL7120
| Category: | PLA+PMMA , Polylactic Acid + PMMA |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | EcoBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O8mZLx_EcoBlend-HCL7120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HCL7120 is a kind of appending 20%~30% biological base plastic environmental PLA/PMMA resin.HCL7120 has excellent mechanical properties and super heat stability.HCL7120 is mainly used in ornament & housing of small appliance,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 5.6 | g/10 min | |
| 240°C/5.0 kg | 5.6 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Biobased Content | 20 to 30 | % | |
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 215 to 225 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5104 Green 3183 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tarnoform® 500 HI4 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Wanthane® WHT-1564 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Gallonprene® GP520-3501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Garaflex™ E 4771-A8 NAT OR-1 LCF | AlphaGary | TPE | Garaflex™ E |