Trithene® TS 7001
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O82Rzs_Trithene-TS-7001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TS 7001 is a low density polyethylene material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TS 7001 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 11.0 | MPa | ASTM D638 |
| Fracture, molding | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 630 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 120 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 130 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 28.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 280 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 210 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 340 | g | ASTM D1922 |
| TD : 50 µm, blown film | 280 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 0.10 to 0.14 g/10 minDensity, ASTM D1505: 0.921 to 0.923 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 185 | °C | |
| Cylinder Zone 2 Temp. | 180 - 195 | °C | |
| Cylinder Zone 3 Temp. | 200 - 210 | °C | |
| Adapter Temperature | 210 - 225 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1Recommended Die Gap: 0.8 to 1.0 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RxLOY™ NEV00NR03NA | Ferro Corporation | PP Alloy | RxLOY™ |
| RTP EMI 330.5D FR | RTP Company | PC | RTP |
| FRAGOM PR/900 ELAS | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| KIBIPOL® PR-255 | CHI MEI CORPORATION | IIR | KIBIPOL® |
| NHU-PPS 21330C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |