PRE-ELEC® ABS 1415
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O7UZNT_PRE-ELEC-ABS-1415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® ABS 1415 has excellent mechanical properties and is easy to extrude. Typical applications include co-extruded multilayer sheets with natural HIPS, ABS or conductive or natural TPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.80 | % | ASTM D955 |
| Flow direction | 0.50 - 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Flow : Yield | 40.0 | MPa | ASTM D638, ISO 527-2 |
| Across Flow | 32.0 | MPa | ASTM D638 |
| Flow | 32.0 | MPa | ASTM D638 |
| -- 1 | 32.0 | MPa | ISO 527-2 |
| 0.400 mm 2 | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Flow : Yield | 4.0 | % | ISO 527-2 |
| Fracture, 0.400mm 3 | 6.0 | % | ISO 527-2 |
| Fracture, 0.400mm 4 | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1930 | MPa | ASTM D790 |
| 4.00 mm | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -20°C | 15 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | 17 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 6 | |||
| -20°C | No Break | ASTM D256 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 8.41 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 14.7 | kJ/m² | ASTM D256 |
| Notched Izod Impact 7 | ISO 180 | ||
| -20°C | 8.0 | kJ/m² | ISO 180 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 60.9 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 8 | ISO 180 | ||
| -20°C | 60 | kJ/m² | ISO 180 |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 87.8 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 88.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 72.8 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 91.1 | °C | ASTM D1525 9 |
| -- | 104 | °C | ASTM D1525, ISO 306/A50 7 10 |
| -- | 91.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+6 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+5 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 230 | °C | |
| Cylinder Zone 5 Temp. | 240 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 240°C |
| Note Message | |
|---|---|
| 1 . | .4 mm Thickness, Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 4 mm thickness |
| 8 . | 4 mm thickness |
| 9 . | 标准 B (120°C/h), 载荷2 (50N) |
| 10 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 50YM240 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Monprene® CP-29048 CLR | Teknor Apex Company | TPE | Monprene® |
| TOPAS® 8007F-600 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Karina BROWN PVC COMPOUND 800-36/217-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 215BB10 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |