Ultraform® S 2320 0035 LEV
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O6OgXn_Ultraform-S-2320-0035-LEV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultraform S 2320 0035 LEV is designed to achieve low emission and smell |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2450 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 11 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 32 | % | ISO 527-2 |
| Tensile Creep Modulus (1000 hr) | 1000 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 210 | kJ/m² | |
| 23°C | 250 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 167 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 6.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 3.45 to 6.89 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E670MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| NuSil MED-4750 | NuSil Technology | Rubber | NuSil |
| HiFill® PBT 2523 | Techmer Engineered Solutions | PBT | HiFill® |
| IDI SMC S20 (Glass Content 10%) | IDI Composites International | TS, Unspecified | IDI SMC |
| LNP™ THERMOCOMP™ RF006EXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |