Ateva® 2842A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O4w52w_Ateva-2842A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (125°C/0.325 kg) | 400 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 67 | ||
| Shore D | 14 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 3.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 600 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 12.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 65.0 | °C | ASTM D3418 |
| Ring and Ball Softening Point | 84 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4970M | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Nypol® PA A3 BGE0209 NR348 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Bergamid™ PA66-MA30 BK001 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ESTABLEND 6500 F | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| PENTAMID A E20 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |