Category: | PPA , Polyphthalamide |
Manufacturer: | Vamp Tech |
Trademark: | DENISTAT |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | O4bZfU_DENISTAT-Z-20G-04-Y.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
PPA/PA 66 20% glass fiber reinforced, surface resistivity 10^4 ohm. |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
Molding Shrinkage | ASTM D955 | ||
Flow | 0.30 | % | |
Across Flow | 0.70 | % |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 16000 | MPa | ASTM D638 |
Tensile Strength (Yield) | 150 | MPa | ASTM D638 |
Tensile Elongation (Break) | 1.4 | % | ASTM D638 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 257 | °C | ASTM D648A |
RTI Elec | 140 | °C | UL 746 |
RTI Imp | 140 | °C | UL 746 |
RTI Str | 140 | °C | UL 746 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 90.0 | °C | |
Drying Time | 3.0 | hr | |
Processing (Melt) Temp | 300 | °C | |
Mold Temperature | 100 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RheTech Polypropylene G13P100-00UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
Celanex® 3300 | Celanese Corporation | PBT | Celanex® |
Galloo rPS-65 | Galloo Plastics | PS (GPPS) | Galloo |
KOPELEN JH-370B | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
MAJORIS CE277 - 8229 | AD majoris | PP, Unspecified | MAJORIS |