| Texin 288 is an aromatic polyester-based thermoplastic polyurethane with a hardness of approximately 88A. It can be processed by injection molding. Extrusion processes are also possible for some applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.54mm | 0.80 | % | ASTM D955 |
| Transverse flow : 2.54mm | 0.80 | % | ASTM D955 |
| Vertical flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 88 | ASTM D2240, ISO 868 | |
| Shaw D | 38 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 46.2 | MPa | ASTM D790, ISO 178 |
| Taber Abrasion Resistance | |||
| 1000 Cycles, 1000g, H-18 wheel | 40.0 | mg | ISO 4649 |
| 1000 Cycles, 1000g, H-18 wheel | 40.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| 100% strain | 6.90 | MPa | ASTM D412, ISO 37 |
| 300% strain | 20.0 | MPa | ASTM D412, ISO 37 |
| Tensile Strength (Yield) | 46.9 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation (Break) | 500 | % | ASTM D412, ISO 37 |
| Tear Strength | |||
| -- 1 | 105 | kN/m | ASTM D624 |
| -- | 110 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 15 | % | ASTM D395 |
| 23°C, 22 hr 2 | 12 | % | ASTM D395B |
| 70°C, 22 hr | 52 | % | ASTM D395 |
| 70°C, 22 hr 3 | 21 | % | ASTM D395B |
| Bayshore Resilience | 41 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -45.0 | °C | DMA |
| Vicat Softening Temperature | 135 | °C | ISO 306/A50, ASTM D1525 4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 99.0 - 110 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 190 - 215 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 205 - 225 | °C | |
| Processing (Melt) Temp | 205 - 215 | °C | |
| Mold Temperature | 15.0 - 40.0 | °C | |
| Injection Pressure | 41.4 - 103 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | < 1.38 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Cushion | < 3.18 | mm |
| Injection instructions |
|---|
| Hold Pressure: 60 to 80% of Injection Pressure |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Post-cured 16 hr at 230°F |
| 3 . | Post-cured 16 hr at 230°F |
| 4 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene M15P101-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| WanBlend® WHT-HF8695 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| NEXT SIGNATURE PPH T40-100 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |
| Flontech® FT-905-DL | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| ElectriPlast® EP-CF/ABS | Integral Technologies, Inc. | ABS | ElectriPlast® |