Beetle® PPC120M 9250
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Beetle® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O33tnw_Beetle-PPC120M-9250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPC120M 9250 is a 20% mineral filled, stabilised polypropylene copolymer black compound intended for extrusion applications. It offers reasonable rigidity and high impact strength, combined with good service life durability over a wide temperature range. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.80 - 1.6 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | ISO 527-2 |
| Fracture | > 200 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 28.0 | MPa | ISO 178 |
| Bending strain- at peak stress | 6.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Melting Temperature | 169 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Teknor Apex test result) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 60.0 | °C | |
| Cylinder Zone 1 Temp. | 190 - 220 | °C | |
| Cylinder Zone 2 Temp. | 190 - 220 | °C | |
| Cylinder Zone 3 Temp. | 190 - 220 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| Maximum Melt temperature 230°CPP materials are not hygroscopic and drying should not normally be necessary.If surface moisture is present on the granules, drying is permissible but temperature should not exceed 60°C to avoid risk of agglomeration. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3200-50NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ELASTOSIL® M 4645 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| INNOPOL® PP CS 2-9000 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Karina BLACK PVC -E 809D48/1-C-IS-AS-LMP (034100/102-00) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND 80/213-D-IS-SI (DAY BRASIL) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |