LNP™ THERMOCOMP™ AF004XXY compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O2fFR6_LNP-THERMOCOMP-AF004XXY-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF004XXY is a compound based on ABS containing 20% glass fiber. Also known as: LNP* THERMOCOMP* Compound AF004XXY Product reorder name: AF004XXY |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.20 | % | |
| Across Flow : 24 hr | 0.40 | % | |
| Water Absorption (24 hr, 50% RH) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6090 | MPa | ASTM D638 |
| -- | 6050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 76.0 | MPa | ASTM D638 |
| Break | 77.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6080 | MPa | ASTM D790 |
| -- 5 | 5970 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 119 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 122 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 7 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 8 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.0 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 100 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4LEX® 9F22120 | 4Plas | PC | 4LEX® |
| Halene L 92001S | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| Plaslube® PA6/6 AF10 HS L | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| TECHNYL® A 218 MV30 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| NORYL™ FE1740PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |